Please select the desired project time frame:
- July 2026
- January 2026
- July 2025
- January 2025
- July 2024
- January 2024
- July 2023
- January 2023
- July 2022
- January 2022
- July 2021
- January 2021
- July 2020
- January 2020
- July 2019
- January 2019
- July 2018
- January 2018
- July 2017
- January 2017
- July 2016
- January 2016
- July 2015
- January 2015
- July 2014
- January 2014
- July 2013
- January 2013
- July 2012
- January 2012
- July 2011
- January 2011
- July 2010
- January 2010
- July 2009
- January 2009
- July 2008
- January 2008
- July 2007
- January 2007
- July 2006
- January 2006
- July 2005
- January 2005
- July 2004
- January 2004
- July 2003
- January 2003
- July 2002
- January 2002
- July 2001
- January 2001
Start of funding 01.01.2015
Thin film deposition under controlled atmosphere using in-situ x-ray scattering
Dr. Eva Herzig
Technische Universität München
Munich School of Engineering (MSE)
Dr. Alexander Hexemer
Lawrence Berkeley National Laboratory
Advanced Light Source
The properties of functional coatings are strongly linked with the molecular morphology of the used materials. It is therefore desirable to gain as much control over the molecular arrangement as possible. While the chemical structure of the new materials plays an important role regarding film morphology, processing parameters have been recognised to be extremely important. Controlling these parameters however is challenging, especially for industrial manufacturing processes like printing, and the influence of the surrounding atmosphere is of utmost importance. The aim of the project is to join the expertise of the two groups to control and examine the influence of the processing parameters during deposition while using in-situ X-ray scattering experiments under grazing incidence geometry at a synchrotron facility. This experimental method reveals structural information with a high time resolution from several hundred to sub-nanometre length scales and is therefore used to systematically examine the morphology and linking it with the properties of organic thin films.
Final report:
A chamber encasing the slot die printer head and the sample allows the systematic control of the surrounding atmosphere during the printing process. Since the drying time has a significant influence on the structure formation in the printed organic thin film, the atmosphere chamber can be used to systematically control the drying time and therefore the structure formation. Apart from adjusting the substrate temperature and the common printing parameters like ink flow rate and deposition speed, the new chamber allows to also vary the atmosphere conditions. A strongly solvent enriched atmosphere therefore slows down the structure formation process, which can be tracked using in situ X-ray scattering and UV-Vis absorption measurements. Thanks to this project it was possible to gain fundamental results on structure formation in printed thin films of a multi-phase system. Further examinations are already ongoing.
Related Publications:
S. Pröller, et al., “Note: Setup for chemical atmospheric control during in situ grazing incidence X-ray scattering of printed thin films”, Review of Scientific Instruments 88, 066101 (2017)
S. Pröller, et al., “Following the morphology formation in situ in printed active layers for organic solar cells”, Advanced Energy Materials 6, 1501580